Secondary Emission Signal of Electron-Beam Welding Zone and Its Connection with Weld Joint Geometric Parameters

Trushnikov D.N., Belenkiy V.Y., Zykov V.V.

Abstract


The emission of electrons from the welding zone is analyzed. Experiments were conducted to examine the spectrum of oscillations of the secondary current at various values of the specific power of the electron beam. The conducted research showed that the signal spectrum of the secondary current in electron beam welding of high power contains a characteristic high-frequency (15 kHz) component. Empirical density distribution of the signal was constructed in the amplitude range for this component. It was shown that the parameters of the density distribution is closely linked with the nature of interaction of the beam with metal and can be used for remote control of technology process.

Keywords


electron beam welding; secondary-emission signals; stainless steel; electron beam focusing; weld formation control and monitoring

References References

Башенко В. В., Мауэр К.-О. Импульсных характер потоков заряженных частиц из канала при электронно-лучевой сварке // Автоматическая сварка. - 1982. - № 3. - С. 62-64.

Батухтин В. А., Башенко В. В. Обработка вторичных излучений для контроля и управления процессом электронно-лучевой сварки // Автоматическое управление технологическим процессом электронно-лучевой сварки. - Киев : ИЭС им. Е. О. Патона, 1987. - С. 64-74.

Pеtrov P., Georgieva C., Petrov G. Experimental investigation of weld pool formation in electron beam welding // Vacuum. - 1998. - Vol. 51, № 3. - P. 339-343.

Беленький В. Я., Язовских В. М., Журавлев А. П. О природе вторичного тока в плазме, образующейся в зоне взаимодействия электронного луча при сварке // Физика и химия обработки материалов. - 1983. - № 6. - С. 128-129.

Krinberg I. A., Mladenov G. M. Formation and expansion of the plasma column under electron beam metal interaction // Vacuum <http://www.sciencedirect.com/science/journal/0042207X>. - 2005. - Vol. 77, № 4. - P. 407-411.

Миткевич Е. А., Локшин В. Е. Динамика формирования канала в условиях электронно-лучевой сварки // Автоматическая сварка. - 1980. - № 9. - С. 26-27. Структура вторично-эмиссионного сигнала при электронно-лучевой сварке с глубоким проплавлением / Д. Н. Трушников [и др.] // Сварка и диагностика. - 2008. - № 4. - С. 22-24.


Article Metrics

Metrics Loading ...

Metrics powered by PLOS ALM

Refbacks

  • There are currently no refbacks.


Copyright (c) 2011 Дмитрий Николаевич Трушников, Владимир Яковлевич Беленький, Виталий Валерьевич Зыков

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.

ISSN 1813-7911