Investigation of the Formation of Structure and Properties in a Billet Made of Heat-Resistant Nickel Alloy EP741NP, Obtained by Hot Isostatic Pressing Technology
DOI:
https://doi.org/10.22213/2413-1172-2023-4-42-49Keywords:
density, hardness, metallographic analysis, heat-resistant nickel alloy, hot isostatic pressingAbstract
It is known that the technology of hot isostatic pressing (HIP) can reduce the residual porosity and increase the level of physical and mechanical characteristics of products obtained by powder metallurgy methods. In modern aircraft and rocket engineering, heat-resistant heterophase nickel alloys are used, which are obtained with the use of granular metallurgy. This material is indispensable in the creation of disks of gas turbine engines (GTE), which are part of the turbine rotor and serve to install the blades. Obtaining a nonporous product made of EP741NP alloy using the HIP technology will increase the service life of the turbine disks, which is an urgent task at the present time. The aim of the work is to study the structure and physical and mechanical properties of a billet made of heat-resistant nickel alloy EP741NP obtained by the HIP method at a temperature of 1150 °C. The starting material for the preparation of the workpiece is a metal powder EP741NP, obtained by gas atomization and having a fractional composition of 20...50 microns. It is shown that the HIP process at a temperature of 1150 °C makes it possible to obtain an optimal combination of physical and mechanical properties. Based on the obtained images of powder particles and the microstructure of the work piece, the shape of the particles of the powder under study, the main category of powder granularity was determined and digital porosity analysis of the workpiece under study was performed in the Thixomet Pro software package. The changes in density and hardness along the section of the work piece were also evaluated. It has been established that at a temperature of HIP 1150 °, the average porosity is insignificant and is 0.1 %, however, as we move away from the edge of the workpiece to its center, there is an increase in the content of pores, the size of which lies in the range of 1...20 microns. It is shown that during the technological process of HIP, an arched effect is observed, the consequence of which are overestimated characteristics of microhardness and density at the edge of the work piece.References
Xu J., Gruber H., Boyd R.D., Jiang S., Peng R.L., Moverare J.J. (2020) On the strengthening and embrittlement mechanisms of an additively manufactured Nickel-base superalloy. Materialia, 2020, p. 100657.
Определение химического состава частиц основных фаз в изделиях из гранулируемого никелевого жаропрочного сплава ЭП741НП / Д. В. Зайцев, С. В. Сбитнева, Л. Б. Бер, А. В. Заводов // Труды ВИАМ. 2016. № 9. С. 61-71.
Шестаков А. В., Карашаев М. М., Дмитриев Н. С. Технологические пути создания композиционных материалов на основе жаропрочных тугоплавких соединений (обзор) / Труды ВИАМ. 2021. № 8. С. 12-20.
Особенности производства заготовок дисков ГТД из гранул высокожаропрочных никелевых сплавов / А. М. Волков, Д. А. Карягин, М. Н. Летников, М. М. Бакрадзе, А. С. Перевозов // Металлург. 2020. № 4. С. 75-80.
Микроструктура и механические свойства никелевого высокопрочного сплава ВЖ172, полученного методом горячего изостатического прессования гранул / И. С. Мазалов, А. М. Волков, Б. С. Ломберг, Е. Б. Чабина // Труды ВИАМ. 2022. № 9. С. 15-27.
Некоторые технологические аспекты производства заготовок методом горячего изостатического прессования капсул с гранулами жаропрочных никелевых сплавов / А. В. Волков, А. Г. Евгенов, В. А. Игнатов, И. Р. Чуманов // Проблемы черной металлургии и материаловедения. 2021. № 1. С. 25-30.
Haocheng Zhang,Anqiang Wang, Zhixun Wen, Zhufeng Yue, Chengjiang Zhang (2016) Effects of Hot Isostatic Pressing (HIP) on Microstructure and Mechanical Propertiesof K403 Nickel-Based Superalloy. HighTemp. Proc., 2016, vol. 35, pp. 463-471.
Sentyurina Zh.A., Baskiv F.A., Loginov P., Kaplanskiy Y., Mishukov A.V., Logachev I.A., Bychkova M.Ya., Levashov E.A., Logacheva A.I. (2021) The effect of hot isostatic pressing and heat treatment on the microstructure and properties of EP741NP nickel alloy manufactured by laser powder bed fusion. Additive Manufacturing, 2021, vol. 37, p. 101629.
Balachandramurthi A.R., Moverare J.J., Dixit N., Deng D., Pederson R. (2019) Microstructural influence on fatigue crack propagation during high cycle fatigue testing of additively manufactured Alloy 718. Acta Materialia, 2019, vol. 168, pp. 287-298.
Goel S., Mehtani H., Yao S.W., Samajdar I., Klement U., Joshi S.V. (2020) As-Built and Post-treated Microstructures of an Electron Beam Melting (EBM) Produced Nickel-Based Superalloy. Metallurgical and Materials Transactions, A, 2020, vol. 51, pp. 6546-6559.
Yunsong Zhao, Siliang He, Longfei Li (2022) Application of Hot Isostatic Pressing in Nickel-Based Single Crystal Superalloys. Crystals, 2022, vol. 12, pp. 805-822.
Влияние технологии ГИП на структуру и свойства никелевого сплава ВЖ159 / А. А. Хлыбов, Е. С. Беляев, А. Д. Рябцев, С. С. Беляева, Ю. А. Гетмановский, П. М. Явтушенко, Д. А. Рябов // Вестник Магнитогорского государственного технического университета им. Г. И. Носова. 2021. Т.19, № 3. С. 75-83.
Lu F., Li L., Antonov S., Zheng Y., Fraser H.L., Wang D., Zhang J., Feng Q. (2020) Еffect of Rе on Long-Tеrm Crеep Behavior of Nickеl-Basеd Single-Crystal Supеralloys for Industrial Gas Turbinе Applications. Superalloys, 2020, pp. 218-227.
Kaplanskii Yu.Yu., Zaitsev A.A., Levashov E.A., Loginov P.A., Sentyurina Zh.A. (2018) NiAl basеd alloy produced by HIP and SLM of prе-alloyed sphеrical powdеrs. Evolution of the structure and mеchanical behavior at high tеmperatures. Matеrials Science and Engineering, A, 2018, vol. 717, pp. 48-59.
Khomutov M.G., Potapkin P., Cheverikin V.V., Petrovskiy P., Travyanov A., Logachev I., Sova A., Smurov I. (2020) Effect of hot isostatic pressing on structure and properties of intermetallic NiAl-Cr-Mo alloy produced by selective laser melting.Intermetallics, 2020, vol. 120, p. 106766.
Liu T., Shi K., Zhao J., Liu S., Zhang Y., Liu H., Chen X., Mei X. (2023) Effect of hot isostatic pressing processing parameters on microstructure and properties of Ti60 high temperature titanium alloy. China Foundry, 2023, vol. 20, pp. 49-56.
Cai C., Pan K., Teng Q., Gao X., Song B., Liu J., Wei Q., Zhou K., Shi Y. (2019) Simultaneously enhanced strength and ductility of FGH4097 nickel-based alloy via a novel hot isostatic pressing strategy. Material Science and Engineering, A, 2019, vol. 760, pp. 19-25.
Teng Q., Xie Y., Sun S., Xue P., Long A., Wu T., Cai C., Guo J., Wei Q. (2022) Anisotropic damage evolution and modeling for a nickel-based superalloy built by additive manufacturing. Journal of Alloys and Compounds, 2022, vol. 909, p. 164668.
Rutter B., Galilea I.L., Theisen W. (2020) An Integrated HIP Hеat-Trеatment of a Singlе Crystal Ni-Basе Superalloy. Supеralloys, 2020, pp. 391-399.
Changhao P., Yuan H., Li B., Ma S. (2022) Anisotropic damage evolution and modeling for a nickel-based superalloy built by additive manufacturing. Engineering Fracture Mechanics, 2022, vol. 263, p. 108450.
Lee J.U., Kim Y.K., Seo S.M., Lee K.A. (2022) Effеcts of hot isostatic prеssing trеatment on thе microstructure and tеnsile propеrties of Ni-basеd supеralloy CM247LC manufacturеd by sеlеctive lasеr melting. Matеrial Sciеnce and Engineеring, 2022, vol. 841, p. 143083.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2024 Александр Анатольевич Хлыбов, Дмитрий Александрович Рябов, Александр Александрович Соловьев, Дмитрий Игоревич Васянкин, Анна Алексеевна Шуянова, Алина Александровна Демченко
This work is licensed under a Creative Commons Attribution 4.0 International License.